Dissertation (MEng(Metallurgical Engineering))--University of Pretoria, 2006.
Saved in:
| Other Authors: | |
|---|---|
| Format: | Thesis |
| Published: |
University of Pretoria
2013
|
| Subjects: | |
| Tags: |
No Tags, Be the first to tag this record!
|
Similar Items: Susceptibility of service exposed creep resistant materials to reheat cracking during repair welding
- Susceptibility of creep aged material to stress relief cracking during repair welding
- The development and validation of a computational fluid dynamics model of an industrial watertube boiler burning bagasse
- The influence of high strength steel on the fatigue life of welded joints in the automotive industry
- Microstructure and mechanical properties of titanium-containing steel weld metal with varying molybdenum and nickel levels before and after thermal cycling
- Model for predicting creep of cracked steel fibre reinforced concrete
- The influence of welding parameters on the sensitisation behaviour of 3CR12