Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter
Dissertation (MSc)--University of Pretoria, 2008.
Saved in:
| Other Authors: | |
|---|---|
| Format: | Thesis |
| Published: |
University of Pretoria
2013
|
| Subjects: | |
| Tags: |
No Tags, Be the first to tag this record!
|
| _version_ | 1867613465059786753 |
|---|---|
| access_status_str | Open Access |
| author2 | Garbers-Craig, Andrie Mariana |
| author_browse | Garbers-Craig, Andrie Mariana |
| author_facet | Garbers-Craig, Andrie Mariana |
| collection | Thesis |
| dc_rights_str_mv | © University of Pretoria 2007 E1082/ |
| description | Dissertation (MSc)--University of Pretoria, 2008. |
| format | Thesis |
| id | oai:repository.up.ac.za:2263/27626 |
| institution | University of Pretoria (South Africa) |
| last_indexed | 2026-06-10T12:36:34.553Z |
| license_str | Other — see source repository |
| provenance_str_mv | Harvested via OAI-PMH from UPSpace — University of Pretoria Institutional Repository |
| publishDate | 2013 |
| publishDateRange | 2013 |
| publishDateSort | 2013 |
| publisher | University of Pretoria |
| publisherStr | University of Pretoria |
| record_format | dspace |
| source_str | UPSpace — University of Pretoria Institutional Repository |
| spelling | oai:repository.up.ac.za:2263/27626 Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter Garbers-Craig, Andrie Mariana michkale@twr.ac.za Kalenga wa Kalenga, Michael Sinter mineralogy Chemicals UCTD Dissertation (MSc)--University of Pretoria, 2008. The sinter quality is dependent on sinter mineralogy, which in turn depends on the chemical compositions of the sinter mix. Although many research works have been conducted, further investigation on the effect of chemical compositions (MgO, A2O3, Basicity) on the sinter quality is still required for further improvement of the sinter and more alternative additives are still being tested. In this project, a sinter pot has been used to manufacture sinters, which were characterized using point-counting to quantify the different phases and X-Ray diffraction to identify the polymorphic forms of Ca2SiO4 of the silicate phases. The produced sinters were evaluated with respect to reducibility index (RI), reduction degradation index (RDI), physical breakdown (TI and AI), and production properties (yield, coke breeze rate and production rate). The influence of ignition temperature, magnesium oxide, alumina addition and basicity on the mineralogy as well as physical and chemical properties of iron ore sinters were investigated. Results were obtained as follows: <ol><li>For the Base case with a basicity of 2, 2.8 mass% MgO content, 1.7 mass % Al2O3 and 10 mass% CaO, the effect of ignition temperature, which ranged between 864oC and 1100oC, on the sinter quality was investigated. Results showed that the ignition temperature had an effect on the sinter properties: reducibility (RI), physical strength (TI and AI), production properties (yield, coke breeze rate and production rate). The temperature 1053oC was the best ignition temperature for an economically acceptable sinter. A further increase in ignition temperature was found to form melt on the surface of the sinter produced, leading to a sinter of low quality. Also, X-rays diffraction pattern showed that the allotropic transformation of the Ca2SiO4did not take place.</li> <li>The Low SiO2– Low Al2O3 sinter had the highest reducibility index and had the highest Abrasion index and the lowest coke breeze rate at 2.8 mass% MgO content compared to all the sinters produced in this project.</li> <li>For the High SiO2 – Low Al2O3 sinter MgO was added through dolomite and fused magnesia. A comparative study on the effect of dolomite and fused magnesia was conducted. The sinter to which fused magnesia was added had lower reducibility, higher reduction degradation, higher tumble index, lower abrasion index and lower coke breeze rate than the sinter to which dolomite was added.</li> <li>High SiO2 – High Al2O3 sinter had the lowest reducibility index, the lowest reduction degradation, the lowest tumbler index and the highest coke breeze rate.</li> <li>The increase in MgO content in all the sinters produced increased the coke breeze rate.</li></ol> Materials Science and Metallurgical Engineering unrestricted 2013-09-07T11:52:21Z 2008-09-05 2013-09-07T11:52:21Z 2007-09-05 2008-09-05 2008-08-29 Dissertation a 2007 E1082/gm http://hdl.handle.net/2263/27626 http://upetd.up.ac.za/thesis/available/etd-08292008-175601/ © University of Pretoria 2007 E1082/ application/pdf University of Pretoria |
| spellingShingle | Sinter mineralogy Chemicals UCTD Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title | Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title_full | Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title_fullStr | Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title_full_unstemmed | Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title_short | Investigation into the influence of magnesia content, alumina content, basicity and ignition temperature on the mineralogy and properties of iron sinter |
| title_sort | investigation into the influence of magnesia content alumina content basicity and ignition temperature on the mineralogy and properties of iron sinter |
| topic | Sinter mineralogy Chemicals UCTD |
| url | http://hdl.handle.net/2263/27626 http://upetd.up.ac.za/thesis/available/etd-08292008-175601/ |